Plastics repair with ABS cement: Difference between revisions

Line 70:

Next is a crack on the same piece.

The lower end of this piece shattered, and left a fracture running up it. The crack is a good candidate for repair.

The lower end of this piece shattered and left a fracture running up it. The crack is a good candidate for repair.

[[Image:inner_crack.01.jpg|170px]]

Line 116:

[[Image:Leftside_top.01.jpg|170px]]

The lines show the fracture ran along the edge, which was reconstituted using ABS cement. As a result, the rounded edge of that corner is gone. It's now a sharp edge, which can easily go unnoticed. The ~~Orange~~ is also significant. That section was gone. Entirely gone. It was rebuilt by making a thin ABS layer, then rebuilding the surface. The rebuilt section was less than perfect, and cracked while back on the bike. This was because the shape it solidified into was not the same as the original shape. After welding the new crack to relieve the stress, it has been doing fine.

The lines show the fracture ran along the edge, which was reconstituted using ABS cement. As a result, the rounded edge of that corner is gone. It's now a sharp edge, which can easily go unnoticed. The orange is also significant. That section was gone. Entirely gone. It was rebuilt by making a thin ABS layer, then rebuilding the surface. The rebuilt section was less than perfect, and cracked while back on the bike. This was because the shape it solidified into was not the same as the original shape. After welding the new crack to relieve the stress, it has been doing fine.

[[Image:Leftside_top.02.jpg|170px]]

===Rebuilding plastic parts from molds.===

@@ Line 70: / Line 70: @@
 Next is a crack on the same piece.
-The lower end of this piece shattered, and left a fracture running up it. The crack is a good candidate for repair.
+The lower end of this piece shattered and left a fracture running up it. The crack is a good candidate for repair.
 [[Image:inner_crack.01.jpg|170px]]
@@ Line 116: / Line 116: @@
 [[Image:Leftside_top.01.jpg|170px]]
-The lines show the fracture ran along the edge, which was reconstituted using ABS cement. As a result, the rounded edge of that corner is gone. It's now a sharp edge, which can easily go unnoticed. The Orange is also significant. That section was gone. Entirely gone. It was rebuilt by making a thin ABS layer, then rebuilding the surface. The rebuilt section was less than perfect, and cracked while back on the bike. This was because the shape it solidified into was not the same as the original shape. After welding the new crack to relieve the stress, it has been doing fine.
+The lines show the fracture ran along the edge, which was reconstituted using ABS cement. As a result, the rounded edge of that corner is gone. It's now a sharp edge, which can easily go unnoticed. The orange is also significant. That section was gone. Entirely gone. It was rebuilt by making a thin ABS layer, then rebuilding the surface. The rebuilt section was less than perfect, and cracked while back on the bike. This was because the shape it solidified into was not the same as the original shape. After welding the new crack to relieve the stress, it has been doing fine.
 [[Image:Leftside_top.02.jpg|170px]]
 ===Rebuilding plastic parts from molds.===